China High Quality Film PFA Suppliers – DY-2020-02 Membrane Grade PVDF – DONGTAI
China High Quality Film PFA Suppliers – DY-2020-02 Membrane Grade PVDF – DONGTAI Detail:
Typital Properties
NO. |
NAME OF INDEX |
UNIT |
INDEX |
1 |
Appearance |
- |
White Transparent Granule |
2 |
Relative Density |
g/cm3 |
1.77-1.79 |
3 |
Melting Point |
℃ |
165-175 |
4 |
Melting flow index |
g/10min |
10-20(5kg) |
5 |
Tensile Strength |
MPa(23℃,≧) |
25 |
6 |
Percentage of breaking elongation |
%(23℃,≧) |
20 |
7 |
Shore hardness type D |
≧ |
70 |
8 |
Moisture Content |
% |
≤0.1 |
9 |
Thermal Decomposition Temperature |
℃ |
382-393 |
The index standard refers to T / FSI 027-2019, and the index data is only for customers’ reference.
Storage and Attention
The products mainly have three packaging forms: two-layer polyethylene plastic bag packaging, carton packaging and ton bag packaging for customers to choose. Daily storage in a clean and dry warehouse to prevent the introduction of impurities. This product is non-toxic and harmless at room temperature, but it should be noted that the processing temperature should not exceed 350 ℃, so as to prevent toxic gas from decomposition.
Product detail pictures:
Related Product Guide:
We've one of the most advanced generation tools, experienced and qualified engineers and workers, recognized good quality manage systems and a friendly skilled product sales workforce pre/after-sales support for China High Quality Film PFA Suppliers – DY-2020-02 Membrane Grade PVDF – DONGTAI , The product will supply to all over the world, such as: Romania, Moscow, Los Angeles, Taking the core concept of "to be the Responsible". We'll redound up on society for high quality merchandise and good service. We will initiative to participate in international competition to be a first- class manufacturer of this product in the world.
By Page from Germany - 2018.12.25 12:43
Products and services are very good, our leader is very satisfied with this procurement, it is better than we expected,
By Raymond from New York - 2018.11.11 19:52